| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0100 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0150 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 2.5 | % |
| 横向流动: 150°C, 30分钟,0.0100 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0150 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 0.40 | % |
机械性能
|
摩擦系数
| 与自身 - 动态 | ASTM D1894 | 0.40 | |
| 与自身 - 动态 | ASTM D1894 | 0.40 | |
| 与自身 - 动态 | ASTM D1894 | 0.40 | |
| 与自身 - 动态 | ASTM D1894 | 0.38 | |
| 与自身 - 静态 | ASTM D1894 | 0.48 | |
| 与自身 - 静态 | ASTM D1894 | 0.48 | |
| 与自身 - 静态 | ASTM D1894 | 0.48 | |
| 与自身 - 静态 | ASTM D1894 | 0.46 | |
| 光学性能 |
雾度
| 10.0 µm | ASTM D1003 | 3.5 | % |
| 12.0 µm | ASTM D1003 | 3.5 | % |
| 15.0 µm | ASTM D1003 | 3.5 | % |
| 23.0 µm | ASTM D1003 | 4.5 | % |