| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0500 mm | ASTM D1204 | 2.0 | % |
| | | | |
| 横向流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0500 mm | ASTM D1204 | 0.40 | % |
| | | | % |
薄膜
| 薄膜厚度 - 经测试 | | | 23，36，50 | µm |
| 可供应的薄膜厚度 | | | 23，36，50 | µm |
抗张强度
| MD: 断裂, 23 µm | ASTM D882 | 186 | MPa |
| MD: 断裂, 36 µm | ASTM D882 | 177 | MPa |
| MD: 断裂, 50µm | ASTM D882 | 167 | MPa |
| | | | |
| TD: 断裂, 23µm | ASTM D882 | 206 | MPa |
| TD: 断裂, 36 µm | ASTM D882 | 186 | MPa |
| TD: 断裂, 50 µm | ASTM D882 | 177 | MPa |
| | | | |
| 伸长率 | MD: 断裂, 23 µm | ASTM D882 | 100 | % |
| MD: 断裂, 36µm | ASTM D882 | 130 | % |
| MD: 断裂, 50 µm | ASTM D882 | 140 | % |
| | | | |
| TD: 断裂, 23 µm | ASTM D882 | 90 | % |
| TD: 断裂, 36µm | ASTM D882 | 120 | % |
| TD: 断裂, 50 µm | ASTM D882 | 130 | % |
| | | | |
| 用量 | 23.0 µm | Internal Method | 31.0 | m²/kg |
| 36.0 µm | Internal Method | 19.8 | m²/kg |
| 50.0 µm | Internal Method | 14.1 | m²/kg |
| | | | |
光学性能
| 雾度 | 23.0 µm | ASTM D1003 | 1.6 | % |
| 36.0 µm | ASTM D1003 | 1.8 | % |
| 50.0 µm | ASTM D1003 | 2.0 | % |
| | | | |
|
透射率
| 23.0 µm | ASTM D1003 | 90 | % |
| 36.0 µm | ASTM D1003 | 90 | % |
| 50.0 µm | ASTM D1003 | 90 | % |