| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 2.0 | % |
| 流动: 150°C, 30分钟, 0.0500 mm | ASTM D1204 | 2.0 | % |
| 流动: 150°C, 30分钟, 0.0750 mm | ASTM D1204 | 1.6 | % |
| | | | |
| 横向流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0500 mm | ASTM D1204 | 0.40 | % |
| 横向流动: 150°C, 30分钟, 0.0750 mm | ASTM D1204 | 0.40 | % |
| | | | % |
薄膜
| 薄膜厚度 - 经测试 | | | 36，50，75 | µm |
| 可供应的薄膜厚度 | | | 36，50，75 | µm |
抗张强度
| MD: 断裂, 36 µm | ASTM D882 | 177 | MPa |
| MD: 断裂, 50 µm | ASTM D882 | 167 | MPa |
| MD: 断裂, 75 µm | ASTM D882 | 167 | MPa |
| | | | |
| TD: 断裂, 36 µm | ASTM D882 | 186 | MPa |
| TD: 断裂, 50 µm | ASTM D882 | 177 | MPa |
| TD: 断裂, 75 µm | ASTM D882 | 177 | MPa |
| | | | |
| 伸长率 | MD: 断裂, 36 µm | ASTM D882 | 130 | % |
| MD: 断裂, 50 µm | ASTM D882 | 140 | % |
| MD: 断裂, 75 µm | ASTM D882 | 150 | % |
| | | | |
| TD: 断裂, 36 µm | ASTM D882 | 120 | % |
| TD: 断裂, 50 µm | ASTM D882 | 130 | % |
| TD: 断裂, 75 µm | ASTM D882 | 130 | % |
| | | | |
| 用量 | 36.0 µm | Internal Method | 19.8 | m²/kg |
| 50.0 µm | Internal Method | 14.3 | m²/kg |
| 75.0 µm | Internal Method | 9.50 | m²/kg |
| | | | |
光学性能
| 雾度 | 36.0 µm | ASTM D1003 | 7.0 | % |
| 50.0 µm | ASTM D1003 | 8.0 | % |
| 75.0 µm | ASTM D1003 | 9.0 | % |
| | | | |
| | | | | |
| | | | |
| | | | |