| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D792 | 1.13 | g/cm3 | | 成型收缩率 | 3.18 mm | ASTM D955 | 0.3 | % | | 吸水率 | 24 hr, 23°C | ASTM D570 | 0.040 | % | | 机械性能 | 洛氏硬度 | | ASTM D785 | 98 | | | 拉伸模量 | | ASTM D638 | 6890 | MPa | | 抗张强度 | | ASTM D638 | 68.9 | MPa | | 拉伸断裂伸长率 | | ASTM D638 | 2.5 | % | | 弯曲模量 | | ASTM D790 | 4830 | MPa | | 弯曲强度 | | ASTM D790 | 103 | MPa | | 压缩强度 | | ASTM D695 | 68.9 | MPa | | 悬壁梁缺口冲击强度 | 3.18 mm | ASTM D256 | 80.1 | J/m | | 无缺口悬臂梁冲击 | 3.18 mm | ASTM D256 | 427 | J/m | | 热性能 | 热变形温度 | 0.45MPa, 未退火 | ASTM D648 | 157 | °C | | 1.8 MPa, 未退火 | ASTM D648 | 146 | °C | | 线形膨胀系数 | | ASTM D696 | 0.000036 | cm/cm/°C | | 导热系数 | | ASTM C177 | 0.33 | W/m/K | | 阻燃等级 | | UL 94 | HB | | | 电气性能 | 体积电阻率 | | ASTM D257 | 1.0E+15 | ohm·cm | | 介电强度 | | ASTM D149 | 20 | kV/mm | | 介电常数 | 1 MHz | ASTM D150 | 2.7 | | | 耗散因数 | 1 MHz | ASTM D150 | 0.0010 | | | 耐电弧性 | | ASTM D495 | 125 | sec | | 加工条件 | 干燥温度 | | | 82.2 | °C | | 干燥时间 | | | 2.0 | hr | | 模具温度 | | | 32-66 | °C | | 注塑温度 | | | 68.9-103 | MPa | | 螺筒后部温度 | | | 218-274 | °C | | 螺筒中部温度 | | | 218-274 | °C | | 螺筒前部温度 | | | 218-274 | °C | | 建议的最大回制料比例 | | | 20 | % | | 背压 | | | 0.345 | MPa | | 螺杆转速 | | | 50-90 | rpm | | 合模力 | | | 6.9-11 | kN/cm² | |