性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能 | 熔流率 | (280°C/2.16 kg) | ASTM D1238 | 15 | g/10 min |
| 吸水率 | (平衡, 23°C, 50% RH) | ASTM D570 | 0.010 | % |
机械性能 | 拉伸模量 | | ASTM D638 | 2150 | MPa |
| | | ASTM D638 | 61.0 | MPa |
| | (断裂) | ASTM D638 | 15 | % |
冲击性能 | 悬壁梁缺口冲击强度 | (3.20 mm) | ASTM D256 | 28 | J/m |
热性能 | 热变形温度 | (1.8 MPa, 未退火) | ASTM D648 | 123 | °C |
| 玻璃转化温度 | | DSC | 140 | °C |
| 线形膨胀系数 | 流动 | ASTM D696 | 0.000070 | cm/cm/°C |
光学性能 | 折射率 | | ASTM D542 | 1.530 | |
| 透射率 | (3000 µm) | ASTM D1003 | 92.0 | % |
补充信息 | The value listed as Melt Flow, ASTM D1238, was tested in accordance with JIS K 6719 (280°C). |
| Abbe Value, Test Method Unspecified: 56 |
| Photoelastic Coefficient, Ellipsometer, 633 nm: 6.3 E-13 cm²/dyne |