| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D792 | 1.15 | g/cm3 | | 成型收缩率 | 3.18 mm | ASTM D955 | 1.0 | % | | 吸水率 | 24 hr, 23°C | ASTM D570 | 0.03 | % | | 机械性能 | 洛氏硬度 | | ASTM D785 | 95 | | | 拉伸模量 | | ASTM D638 | 3170 | MPa | | 抗张强度 | | ASTM D638 | 33.8 | MPa | | 断裂伸长率 | | ASTM D638 | 7.5 | % | | 弯曲模量 | | ASTM D790 | 2760 | MPa | | 弯曲强度 | | ASTM D790 | 55.2 | MPa | | 压缩强度 | | ASTM D695 | 49.6 | MPa | | 悬壁梁缺口冲击强度 | 3.18 mm | ASTM D256 | 26.7 | J/m | | 无缺口悬臂梁冲击 | 3.18 mm | ASTM D256 | 251 | J/m | | 热性能 | 热变形温度 | 0.45MPa, 未退火 | ASTM D648 | 135 | °C | | 1.8 MPa, 未退火 | ASTM D648 | 79.4 | °C | | 线形膨胀系数 | | ASTM D696 | 0.000049 | cm/cm/°C | | 导热系数 | | ASTM C177 | 0.3 | W/m/K | | 阻燃等级 | | UL 94 | HB | | | 电气性能 | 体积电阻率 | | ASTM D257 | 1.0E+16 | ohm·cm | | 介电强度 | | ASTM D149 | 20 | kV/mm | | 介电常数 | 1 MHz | ASTM D150 | 2.6 | | | 耗散因数 | 1 MHz | ASTM D150 | 0.006 | | | 耐电弧性 | | ASTM D495 | 120 | sec | | 加工条件 | 干燥温度 | | | 82.2 | °C | | 干燥时间 | | | 2.0 | hr | | 模具温度 | | | 32.2-65.6 | °C | | 注塑温度 | | | 68.9-138 | MPa | | 螺筒后部温度 | | | 232-274 | °C | | 螺筒中部温度 | | | 232-274 | °C | | 螺筒前部温度 | | | 232-274 | °C | | 建议的最大回制料比例 | | | 20 | % | |