性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能 | 比重 | | ASTM D792 | 0.95 | g/cm³ |
| 熔流率 | (260°C/2.16 kg) | ISO 1133 | 7.0 | g/10 min |
| 吸水率 | (平衡) | ASTM D570 | 0.010 | % |
机械性能 | 拉伸模量 | | ISO 527-2 | 1700 | MPa |
| 拉伸应力 | (屈服) | ISO 527-2 | 45.0 | MPa |
| 拉伸应变 | (断裂) | ISO 527-2 | 140 | % |
| 弯曲模量 | | ISO 178 | 1600 | MPa |
| 弯曲强度 | | ISO 178 | 64.0 | MPa |
冲击性能 | 悬壁梁缺口冲击强度 | (3.20 mm) | ASTM D256 | 510 | J/m |
热性能 | 热变形温度 | (1.8 MPa, 未退火) | ISO 75-2/A | 110 | °C |
| 玻璃转化温度 | (DSC) | DSC | 136 | °C |
| 线形膨胀系数 | 流动 | ASTM D696 | 0.000070 | cm/cm/°C |
电气性能 | 体积电阻率 | | IEC 60093 | 1.0E+16 | ohm·cm |
| 介电强度 2 (1.00 mm) | 方法A(短时间) | ASTM D149 | 40 | kV/mm |
| 介电常数 (1 MHz) | | IEC 60250 | 2.30 | |
| 耗散因数 (1 MHz) | | IEC 60250 | 0.00020 | |
可燃性 | UL 阻燃等级 | | UL 94 | HB | |
补充信息 | The value listed as Melt Mass - Flow Rate ISO 1133, was tested in accordance with JIS K6719. |
| Water Absorption, ASTM D570: <0.01 % |
| Pencil Hardness, JIS K5401: B |
| Light Transmittance, ASTM D1003, 3 mm: white opaque |