性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能 | 比重 | | ASTM D792 | 1.01 | g/cm³ |
| 熔流率 | (280°C/2.16 kg) | ASTM D1238 | 27 | g/10 min |
| 收缩率 | 流动 | ASTM D955 | | % |
| 吸水率 | (平衡, 23°C, 50% RH | ASTM D570 | 0.010 | % |
机械性能 | 拉伸模量 | | ASTM D638 | 1700 | MPa |
| | (屈服) | ASTM D638 | 50.0 | MPa |
| | (屈服) | ASTM D638 | 100 | % |
| 弯曲模量 | | ASTM D790 | 1900 | MPa |
| 弯曲强度 | | ASTM D790 | 65.0 | MPa |
热性能 | 热变形温度 | (1.8 MPa, 未退火) | ASTM D648 | 68.0 | °C |
| 玻璃转化温度 | | DSC | 70.0 | °C |
| 线形膨胀系数 | 流动 | ASTM D696 | 0.000070 | cm/cm/°C |
电气性能 | 体积电阻率 | | ASTM D257 | | ohm·cm |
| 介电强度 | | ASTM D149 | 70 | kV/mm |
| 介电常数 (1 MHz) | | ASTM D150 | 2.3 | |
可燃性 | UL 阻燃等级 | | UL 94 | HB | |
光学性能 | 折射率 | | ASTM D542 | 1.530 | |
| 透射率 | (3000 µm) | ASTM D1003 | 92.0 | % |
补充信息 | Moisture Permeability, JIS Z 0280: 0.28 g/m² 24hr |
| Thermal decomposition temperature, No standard: 420 °C |
| IZOD Impact Strength, ASTM D256: 9 KJ/m² |
| Dupont Impact Strength, ASTM D256: 35J |
| Dielectric loss tangent, ASTM D150, 1MHz: 0.0002 |