| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D792 | 1.24 | g/cm3 | | 成型收缩率 | 3.18 mm, 注塑 | ASTM D955 | 1.0 | % | | 6.35 mm, 注塑 | ASTM D955 | 1.4 | % | | 吸水率 | 24 hr, 23°C | ASTM D570 | 0.02 | % | | 机械性能 | 洛氏硬度 | | ASTM D785 | 99 | | | 拉伸模量 | 注塑 | ASTM D638 | 2890 | MPa | | 抗张强度 | | ASTM D638 | 24.0 | MPa | | 伸长率 | 屈服, 注塑 | ASTM D638 | 10 | % | | 弯曲模量 | 注塑 | ASTM D790 | 2480 | MPa | | 弯曲强度 | 注塑 | ASTM D790 | 48.0 | MPa | | 压缩强度 | | ASTM D695 | 50.0 | MPa | | 悬壁梁缺口冲击强度 | 3.18 mm, 注塑 | ASTM D256 | 32.0 | J/m | | 无缺口悬臂梁冲击 | 3.18 mm | ASTM D256 | 1070 | J/m | | 热性能 | 热变形温度 | 0.45 MPa, 未退火, 注塑 | ASTM D648 | 121 | °C | | 1.8 MPa, 未退火, 注塑 | ASTM D648 | 77.0 | °C | | 线形膨胀系数 | | ASTM D696 | 0.000050 | cm/cm/°C | | 导热系数 | | ASTM C177 | 0.29 | W/m/K | | 阻燃等级 | | UL 94 | HB | | | 电气性能 | 介电强度 | | ASTM D149 | 220 | kV/mm | | 介电常数 | 1 MHz | ASTM D150 | 3.1 | | | 耗散因数 | 1 MHz | ASTM D150 | 0.007 | | | 耐电弧性 | | ASTM D495 | 128 | sec | | 加工条件 | 模具温度 | | | 32.0-66.0 | °C | | 注塑温度 | | | 69.0-103 | MPa | | 螺筒后部温度 | | | 193-227 | °C | | 螺筒中部温度 | | | 193-227 | °C | | 螺筒前部温度 | | | 193-227 | °C | |