| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | -- | ASTM D792 | 1.35 | g/cm³ |
| | | -- | ISO 1183 | 1.34 | g/cm³ |
| | 熔流率 | 250°C/2.16kg | ASTM D1238 | 9.6 | g/10 min |
| | 溶化体积流率 MVR | 250°C/2.16 kg | ISO 1133 | 8.00 | cm³/10min |
| | 收缩率 | 流动 2 | Internal Method | 1.1-1.8 | % |
| | | 流动: 3.20 mm | Internal Method | 1.0-1.4 | % |
| | | 横向流动 2 | Internal Method | 0.90-1.8 | % |
| | 吸水率 | 饱和, 23°C | ISO 62 | 0.50 | % |
| | | 平衡, 23°C, 50% RH | ISO 62 | 0.15 | % |
| | 洛氏硬度 | R 计秤 | ISO 2039-2 | 117 | |
| | 球压硬度 | H 358/30 | ISO 2039-1 | 111 | MPa |
| 机械性能 | 拉伸模量 | -- 3 | ASTM D638 | 2020 | MPa |
| | | -- | ISO 527-2/1 | 2200 | MPa |
| | 抗张强度 | | ASTM D638 | 48.0 | MPa |
| | | 屈服 | ISO 527-2/50 | 50.0 | MPa |
| |
| 断裂 4 | ASTM D638 | 41.0 | MPa |
| |
| 断裂 | ISO 527-2/50 | 40.0 | MPa |
| | 伸长率 | 屈服 4 | ASTM D638 | 5.0 | % |
| | | 屈服 | ISO 527-2/50 | 5.0 | % |
| | | 断裂 4 | ASTM D638 | 54 | % |
| | | 断裂 | ISO 527-2/50 | 30 | % |
| | 弯曲模量 | 50.0 mm 跨距 5 | ASTM D790 | 2100 | MPa |
| | | -- 6 | ISO 178 | 2000 | MPa |
| | 弯曲强度
| -- 6.7
| ISO 178 | 80.0 | MPa |
| | | 屈服, 50.0 mm 跨距 5 | ASTM D790 | 78.0 | MPa |
| | 抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 转轮 | Internal Method | 33.0 | mg |
| | 简支梁缺口冲击强度 | -30°C 8 | ISO 179/1eA | 20 | kJ/m² |
| | | 23°C 8 | ISO 179/1eA | 45 | kJ/m² |
| | | 23°C | ISO 179/2C | 15 | kJ/m² |
| | 简支梁缺口冲击强度 8 | -30°C | ISO 179/1eU | 无断裂 | |
| | | 23°C | ISO 179/1eU | 无断裂 | |
| | 悬壁梁缺口冲击强度 | -30°C | ASTM D256 | 150 | J/m |
| | | 23°C | ASTM D256 | 320 | |
| | | -30°C 9 | ISO 180/1A | 10 | |
| | | 23°C 9 | ISO 180/1A | 45 | |
| | 无缺口伊佐德冲击强度 9 | -30°C | ISO 180/1U | 无断裂 | |
| | | 23°C | ISO 180/1U | 无断裂 | |
| | 装有测量仪表的落镖冲击 | 23°C, Energy at Peak Load | ASTM D3763 | 35.0 | J |
| 热性能 | 热变形温度
| 0.45 MPa, 未退火, 100 mm 跨距 10 | ISO 75-2/Be | 135 | °C |
| | | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 98.0 | °C |
| | | 1.8 MPa, 未退火, 1000 mm 跨距 10 | ISO 75-2/Ae | 85.0 | °C |
| | | 1.8 MPa, 未退火, 64.0 mm 跨距 11 | ISO 75-2/Af | 84.0 | °C |
| | 维卡软化温度 | -- | ASTM D1525 12 | 134 | °C |
| | | -- | ISO 306/A50 | 180 | °C |
| | | -- | ISO 306/B50 | 145 | °C |
| | | -- | ISO 306/B120 | 150 | °C |
| | Ball Pressure Test | 125°C | IEC 60695-10-2 | pass | |
| | 线形膨胀系数 | 流动: -40 到 40°C | ASTM E831 | 0.000092 | cm/cm/°C |
| | | 流动: 23 到 80°C | ISO 11359-2 | 0.00010 | cm/cm/°C |
| | | 横向: -40 到 40°C | ASTM E831 | 0.000084 | cm/cm/°C |
| | | 横向: 23 到 80°C | ISO 11359-2 | 0.00010 | cm/cm/°C |
| | 导热系数 | | ISO 8302 | 0.17 | W/m/K |
| 电气性能 | 表面电阻率 | | IEC 60093 | >1.0E+15 | ohms |
| | 体积电阻率 | | IEC 60093 | >1.0E+15 | ohm·cm |
| | 相对电容率 | 50 Hz | IEC 60250 | 3.00 | |
| | | 60 Hz | IEC 60250 | 3.00 | |
| | | 1 MHz | IEC 60250 | 2.90 | |
| | 耗散因数 | 50 Hz | IEC 60250 | 0.0020 | |
| | | 60 Hz | IEC 60250 | 0.0020 | |
| | | 1 MHz | IEC 60250 | 0.0070 | |
| | 漏电起痕指数 | -- | IEC 60112 | 225 | V |
| | | 解决方案 B | IEC 60112 | 100 | V |
| | 耐电强度 | 0.800 mm, 在油中 | IEC 60243-1 | 34 | kV/mm |
| | | 1.60 mm, 在油中 | IEC 60243-1 | 26 | kV/mm |
| | | 3.20 mm, 在油中 | IEC 60243-1 | 18 | kV/mm |
| 可燃性 | UL 阻燃等级 | 0.750 mm | UL 94 | V-0 | |
| | | 2.50 mm | UL 94 | 5VA | |
| | 灼热丝易燃指数 | 1.00 mm | IEC 60695-2-12 | 960 | °C |
| | 极限氧指数 | | ISO 4589-2 | 30 | % |