| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 |
| ASTM D792, ISO 1183 | 1.39 | g/cm³ |
| | 溶流率 | 250°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| | 溶化体积流率 MVR | 250°C/1.2 kg | ISO 1133 | 9.00 | cm³/10min |
| | 收缩率 | | Internal Method | 0.60-0.90 | % |
| | | 流动: 3.20 mm | Internal Method | 0.60-1.6 | % |
| | | 横向流动 2
| Internal Method | 0.70-1.0 | % |
| | 吸水率 | 饱和, 23°C | ISO 62 | 0.20 | % |
| | | 平衡, 23°C, 50% RH | ISO 62 | 0.070 | % |
| | 球压硬度 | H 358/30 | ISO 2039-1 | 117 | MPa |
| 机械性能 | 拉伸模量 | -- 3 | ASTM D638 | 4600 | MPa |
| | | -- | ISO 527-2/1 | 4500 | MPa |
| | 抗张强度 | 屈服 4 | ASTM D638 | 75.0 | MPa |
| | | 屈服 | ISO 527-2/5 | 72.0 | MPa |
| | | 断裂 4 | ASTM D638 | 75.0 | MPa |
| | | 断裂 | ISO 527-2/5 | 72.0 | MPa |
| | 伸长率 | 屈服 4 | ASTM D638 | 3.0 | % |
| | | 屈服 | ISO 527-2/5 | 4.0 | % |
| | | 断裂 4 | ASTM D638 | 3.0 | % |
| | | 断裂 | ISO 527-2/5 | 4.0 | % |
| | 弯曲模量 | 50.0 mm 跨距 5 | ASTM D790 | 3940 | MPa |
| | | -- 6 | ISO 178 | 3500 | MPa |
| | 弯曲强度 | | ISO 178 | 110 | MPa |
| | | 屈服, 50.0 mm 跨距 5 | ASTM D790 | 110 | MPa |
| | 简支梁缺口冲击强度 8 | -30°C | ISO 179/1eA | 6.0 | kJ/m² |
| | | 23°C | ISO 179/1eA | 7.0 | kJ/m² |
| | 简支梁缺口冲击强度 8 | -30°C | ISO 179/1eU | 45 | kJ/m² |
| | | 23°C | ISO 179/1eU | 45 | kJ/m² |
| | 悬壁梁缺口冲击强度 | -30°C | ASTM D256 | 74 | |
| | | 23°C | ASTM D256 | 74 | |
| | | -30°C 9 | ISO 180/1A | 6.0 | kJ/m² |
| | | 23°C 9 | ISO 180/1A | 6.0 | kJ/m² |
| | 无缺口伊佐德冲击强度 9 | -30°C | ISO 180/1U | 37 | kJ/m² |
| | | 23°C | ISO 180/1U | 37 | kJ/m² |
| | 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 4.00 | J |
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 100 mm 跨距 10 | ISO 75-2/Be | 215 | °C |
| | | 1.8 MPa, 未退火, 3.20mm 跨距 | ASTM D648 | 175 | °C |
| | | 1.8 MPa, 未退火, 1000 mm 跨距 10
| ISO 75-2/Ae | 170 | °C |
| | 维卡软化温度 | -- | ASTM D1525 11, ISO 306/B50 11 | 205 | °C |
| | | -- | ISO 306/B120 | 208 | °C |
| | Ball Pressure Test | 125°C | IEC 60695-10-2 | pass | |
| | 线形膨胀系数 | 流动: -40 到40°C | ASTM E831 | 0.000060 | cm/cm/°C |
| | | | ISO 11359-2 | 0.000060 | cm/cm/°C |
| | | 横向: -40 到 40°C | ASTM E831 | 0.000080 | |
| | | 横向: 23 到 80°C | ISO 11359-2 | 0.000080 | cm/cm/°C |
| | | 横向: 23 到 150°C | ISO 11359-2 | 0.000085 | cm/cm/°C |
| 电气性能 | 表面电阻率 | | IEC 60093 | >1.0E+15 | ohms |
| | 体积电阻率 | | IEC 60093 | >1.0E+15 | ohm·cm |
| | 相对电容率 | 50 Hz | IEC 60250 | 3.10 | |
| | | 60 Hz | IEC 60250 | 3.10 | |
| | | 1 MHz | IEC 60250 | 3.00 | |
| | 耗散因数 | 50 Hz | IEC 60250 | 0.0010 | |
| | | 60 Hz | IEC 60250 | 0.0010 | |
| | | 1 MHz | IEC 60250 | 0.014 | |
| | 漏电起痕指数 | -- | IEC 60112 | 250 | V |
| | | 解决方案 B | IEC 60112 | 150 | V |
| | 耐电强度 | 0.800 mm, 在油中 | IEC 60243-1 | 30 | kV/mm |
| | | 1.60 mm, 在油中 | IEC 60243-1 | 25 | kV/mm |
| | | 3.20 mm, 在油中 | IEC 60243-1 | 17 | kV/mm |
| 可燃性 | UL 阻燃等级 | 0.60 mm, Testing by SABIC | UL 94 | HB | |
| | 灼热丝易燃指数 | 1.00 mm | IEC 60695-2-12 | 750 | °C |