| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 其它性能 | 比重 | | ASTM D-792 | 1.22 | |
| 机械性能 | 压缩调整 | 22 hours @ 70℃ | | 65 | % |
| Brookfield Viscosity | 15% T.S.in THF | RVT Spindle #2,20 RPM,23℃ | 600 | cps |
| 100%模量伸长率 | | ASTM D-412（ASTM D-638） | 9.7 | MPa |
| 拉伸强度 | | ASTM D-412（ASTM D-638） | 50.3 | MPa |
| 断裂强度 | | ASTM D-624，Die C | 92.8 | KN/m |
| Taber Abrasion | CS-17 wheel,1000g load | ASTM D-1044 | 2.6 | mg/1000 cycles |
| 极限伸长率 | | ASTM D-412（ASTM D-638） | 380 | % |
| Split Tear Resistance | | ASTM D-470 | 68.3 | KN/m |
| 洛氏硬度 | | ASTM D-2240 | 90A（45D） | |
| 压缩调整 | 22 hours @ 23℃ | | 18 | % |
| 300%模量伸长率 | | ASTM D-412（ASTM D-638） | 34.5 | MPa |
| Adhesion to PET | Cast in THF | TP-141 | 0.04 | KN/m |
| 拉伸调整 | | ASTM D-412 | 17 | % |
| 热性能 | 维卡软化点 | | ASTM D-1525 | 92 | ℃ |
| 玻璃化转变温度 | | DSC | -3 | ℃ |
| 其它性能 | Open Time | | ASTM D-4497-94 | ＜5 | sec |
| Gradient Bar Tack Temperature | | | 161 | ℃ |
| T-peel,Mylar Film | | ASTM D-1876-72 | 2.3 | KN/m |
| Ring and Ball Softening Point | | ASTM E-28-92 | 187 | ℃ |
| T-peel,Aluminum Foil | | ASTM D-1876-72 | 0.4 | KN/m |
| Melt Viscosity @ 204 C(400℃) | | ASTM D-1084-88 | 85,000 | cps |