| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 230°C/2.16 kg | ASTM D1238 | 3.2 | g/10min |
| 物理性能 | 比重 | | ASTM D792 | 0.9 | G/cm3 |
| 机械性能 | 割线模数 | | ASTM D882 | | 2% Secant, TD: 50.0 µm | 2% Secant, MD: 50.0 µm | | 1140 | 1170 |
| Mpa |
| 抗张强度 | | ASTM D882 | | MD: Yield, 50.0 µm | MD: Break, 50.0 µm | TD: Break, 50.0 µm | TD: Yield, 50.0 µm | | 27 | 38 | 39 | 41 |
| Mpa |
| 抗张伸展率 | | ASTM D882 | | MD: Break, 50.0 µm | TD: Break, 50.0 µm | | 250 | 6 |
| % |
| 热性能 | 熔化温度 | | | 162-166 | ℃ |
| 光学性能 | 光泽度 | 45°, 50.0 µm | ASTM D2457 | 32 | |
| 雾度 | 50.0 µm | ASTM D1003 | 23 | % |