| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 密度 | | ASTM D-792 | 0.959 | g/cm3 |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 8 | g/10min |
| 机械性能 | 环境应力开裂 | 50℃，2mm，100% Igepal，Compression Molded，F50 | ASTM D-1693B | 5 | hr |
| 邵氏硬度 | Shore D，15 sec，Compression Molded | ASTM D-2240 | 63 | |
| 拉伸屈服强度 | Compression Molded | ASTM D-638 | 29 | MPa |
| 拉伸屈服伸长率 | Compression Molded | ASTM D-638 | 7.5 | % |
| 弯曲模量-2% Secant | Compression Molded | ASTM D-790 | 1140 | MPa |
| IZOD缺口冲击强度 | Compression Molded | ASTM D-256 | 35 | J/m |
| 热性能 | 热变形温度 | 0.45MPa, Unannealed，Compression Molded | ASTM D-648 | 76 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 126 | ℃ |