| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 密度 | | ASTM D-792 | 0.955 | g/cm3 |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min |
| 机械性能 | 环境应力开裂 | 50℃，2mm，100% Igepal，Compression Molded，F50 | ASTM D-1693B | 1 | hr |
| 邵氏硬度 | Shore D，15 sec，Compression Molded | ASTM D-2240 | 64 | |
| 拉伸屈服强度 | Compression Molded | ASTM D-638 | 28 | MPa |
| 拉伸屈服伸长率 | Compression Molded | ASTM D-638 | 7.2 | % |
| 弯曲模量 | Compression Molded | ASTM D-790 | 1060 | MPa |
| IZOD缺口冲击强度 | Compression Molded | ASTM D-256 | 25 | J/m |
| 热性能 | 热变形温度 | 0.45MPa，Unannealed，Compression Molded | ASTM D-648 | 75 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 124 | ℃ |