| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D792, ISO 1183 | 1.07 | g/cm³ | | | 溶化体积流率 | MVR 220°C/10.0 kg | ASTM D1238, ISO 1133 | 4.00 | cm³/10min | | | 收缩率 | 流动 | ASTM D955 | 0.55 | % | | | 吸水率 | 饱和, 23℃ | ASTM D570 | 1.7 | % | | 硬度 | 洛氏硬度 | R 计秤 | ASTM D785 | 89 | | | 机械性能 | 拉伸模量 | 23℃ | ASTM D638 | 1650 | MPa | | | 抗张强度 | 屈服, 23℃ | ASTM D638 | 33.0 | | | | 伸长率 | 屈服, 23℃ | ASTM D638 | 2.7 | % | | | 弯曲模量 | 23℃ | ASTM D790 | 1660 | MPa | | | 弯曲强度 | 23℃ | ASTM D790 | 47.0 | MPa | | | 简支梁缺口冲击强度 | -40℃ | ASTM D256 | 51 | J/m | | | | 23℃ | ASTM D256 | 260 | J/m | | 热性能 | 热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 101 | ℃ | | | | 1.8 MPa, 未退火 | ASTM D648 | 83.0 | ℃ | | | 维卡软化温度 | | ASTM D1525 3 | 92.0 | ℃ | | | 线形膨胀系数 | 流动
| ISO 11359-2 | 0.000095 | cm/cm/℃ | | 电气性能 | 表面电阻率 | | ASTM D257, IEC 60093 | >1.0E+13 | ohm | | | 体积电阻率 | | ASTM D257, IEC 60093 | >1.0E+14 | ohm·cm | | | 介电常数 | 1.00 mm, 1 MHz | ASTM D150 | 3.40 | | | | | | IEC 60250 | 3.80 | | | | | 1 MHz | IEC 60250 | 3.40 | | | | 耗散因数 | 100 Hz | IEC 60250 | 0.0090 | | | | | 1 MHz | IEC 60250 | 0.034 | | | | 漏电起痕指数 | | IEC 60112 | 600 | V | | | 耐电强度 | | IEC 60243-1 | 35 | kV/mm | | 其他 | Gardner光泽度 | 60° | ASTM D523 | 48 | | |