| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 300°C/1.2 kg | ASTM D1238 | 15 | g/10 min |
| 吸水率 | 24 hr, 23°C | ASTM D570 | 0.15 | % |
| 吸水率 | Equilibrium, 23°C, 50% RH | ASTM D570 | 0.32 | % |
| 物理性能 | 比重 | | ASTM D792 | 1.2 | g/cm3 |
| 模件收缩率 | | ASTM D955 | 0.5-0.7 | % |
| 机械性能 | 硬度 | M-Scale | ASTM D785 | 72 | |
| 硬度 | R-Scale | ASTM D785 | 118 | |
| 拉伸模量 | | ASTM D638 | 2340 | Mpa |
| 屈服抗张强度 | 23°C | ASTM D638 | 60 | Mpa |
| 断裂抗张伸展率 | | ASTM D638 | 150 | % |
| 弯曲模量 | | ASTM D790 | 2410 | Mpa |
| 弯曲强度 | | ASTM D790 | 96.5 | Mpa |
| 耐磨性 | 1000 g; CS-10 F wheel; 500 cycles | ASTM D1044 | 45 | % |
| 缺口冲击强度 | 230°C, 3.18 mm | ASTM D256 | 854 | J/m |
| 仪器化落锤冲击强度 | 230°C, 3.18 mm, Total Energy | ASTM D3763 | 87 | J |
| 断裂抗张强度 | | ASTM D638 | 70 | Mpa |
| 屈服抗张伸展率 | | ASTM D638 | 6 | % |
| 电气性能 | 体积电阻率 | 23°C | ASTM D257 | 2.0E+17o | ohm.cm |
| 介电常数 | 60HZ | ASTM D50 | 3 | |
| 介电损耗 | 60HZ | ASTM D150 | 0.001 | |
| 相对漏电起痕指数 | 2.00mm | ICE 60112 | 250 | V |
| 热性能 | 退火热变形温度 | 0.45MPa, 4.00 mm143°C | ASTM D648 | 143 | ℃ |
| 热变形温度 | 1.8 MPa,退火4.00 mm | ASTM D648 | 127 | ℃ |
| 热变形温度 | 0.45MPA，未退火 | ASTM D648 | 140 | ℃ |
| 维卡软化点 | | ASTM D1525 | 148 | ℃ |
| 压痕温度 | | IEC 60589-1 | ＞125 | ℃ |
| CLTE-流 | | ASTM D696 | 0.000068 | cm/cm/℃ |
| 其它性能 | 绝缘强度 | | ASTM D149 | 17 | KV/mm |
| 火焰等级 | 1.60mm | UL 94 | HB | |
| 火焰等级 | 3.20mm | UL 94 | HB | |
| 电线着火温度 | 2.00 mm, 5.0 sec | CIEC 60695-2-13 | 850 | ℃ |
| 氧指数 | | ASTM D2863 | 26 | % |
| 平均燃烧值 | | ASTM D635 | 3 | cm |
| 光学性能 | 折射率 | | ASTM D542 | 1.586 | % |
| 透光率 | | ASTM D1003 | 89 | % |
| 雾度 | | ASTM D1003 | 0.7-1.5 | % |