【PBT|6130C NC010|美国杜邦】规格_用途_参数_物性表

品种：PBT|6130C NC010

生产企业：美国杜邦

打印

规格用途

规格级别	其它其它注塑	外观颜色
该料用途
备注说明

技术参数

性能项目			试验条件[状态]	测试方法	测试数据	数据单位
物理性能	收缩率		平行流动方向	ASTM D955	0.016	cm/cm
物理性能	收缩率		垂直流动方向	ASTM D955	0.016	cm/cm
机械性能	弯曲模量		90 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	331	Mpa
	弯曲模量		（-40 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	3000	Mpa
	弯曲模量		23 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	2410	Mpa
	弯曲模量		149 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	234	Mpa
	弯曲强度		90 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	13	Mpa
	弯曲强度		（-40 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	120	Mpa
	弯曲强度		23 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	80	Mpa
	弯曲强度		149 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	8	Mpa
	断裂点伸长率	-	90 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
		-	-40 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	11	%
		-	23 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
		-	150 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
	非缺口冲击强度	-	-40 °C, 0.00 mm	ASTM D256	No Break	J/m
	非缺口冲击强度	-	23 °C, 0.00 mm	ASTM D256	No Break	J/m
热性能	熔点			DSC	225	℃
	阻燃性	-	3.00 mm	UL94	HB
		-	1.5mm	UL94	HB
		-	0.81mm	UL94	HB
其它性能	极限氧指数		3.20 mm	ASTM D2863	22	%