| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 2.2 | % |
| 流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 2.2 | % |
| | | | |
| | | | |
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.0 | % |
| 横向流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 0.0 | % |
| | | | |
| | | | |
薄膜
| 薄膜厚度 - 经测试 | | | 12，23 | µm |
| 可供应的薄膜厚度 | | | 12，23 | µm |
抗张强度
| MD: 断裂, 12 µm | ASTM D882 | 216 | MPa |
| MD: 断裂, 23 µm | ASTM D882 | 196 | MPa |
| | | | |
| | | | |
| TD: 断裂, 12µm | ASTM D882 | 226 | MPa |
| TD: 断裂, 23µm | ASTM D882 | 206 | MPa |
| | | | |
| | | | |
| 伸长率 | MD: 断裂, 12 µm | ASTM D882 | 100 | % |
| MD: 断裂, 23µm | ASTM D882 | 100 | % |
| | | | |
| | | | |
| TD: 断裂, 12 µm | ASTM D882 | 95 | % |
| TD: 断裂, 23µm | ASTM D882 | 95 | % |
| | | | |
| | | | |
| 用量 | 12.0 µm | Internal Method | 59.5 | m²/kg |
| 23.0 µm | Internal Method | 31.0 | m²/kg |
| | | | |
| | | | |
| 水蒸气透过性 | -- 3 | ASTM F1249 | | g/m²/24 hr |
| -- 4 | ASTM F1249 | | g/m²/24 hr |
| | | | |
| | | | |
| Optical Density | 12.0 µm | Internal Method | -2.8 到 7.2 | % |
| 23.0 µm | Internal Method | -2.8 到 7.2 | % |
| | | | |