| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 2.5 | % |
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.4 | % |
| 横向流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 0.4 | % |
| | 表面张力 | Metallized side (12.0 µm) | ASTM D2578 | 56 | dyne/cm |
| | Metallized side (23.0 µm) | ASTM D2578 | 56 | dyne/cm |
薄膜
| 薄膜厚度 - 经测试 | | | 12,23 | µm |
| 可供应的薄膜厚度 | | | 12,23 | µm |
抗张强度
| MD: 断裂, 12 µm | ASTM D882 | 186 | MPa |
| MD: 断裂, 23 µm | ASTM D882 | 186 | MPa |
| TD: 断裂, 12µm | ASTM D882 | 196 | MPa |
| TD: 断裂, 23 µm | ASTM D882 | 196 | MPa |
| 伸长率 | MD: 断裂, 12 µm | ASTM D882 | 90 | % |
| MD: 断裂, 23 µm | ASTM D882 | 90 | % |
| TD: 断裂, 12 µm | ASTM D882 | 85 | % |
| TD: 断裂, 23 µm | ASTM D882 | 85 | % |
| 透氧率 | (23°C, 12 µm) | ASTM D3985 | < 1.000 | cm³/m²/24 hr |
| (23°C, 23 µm) | ASTM D3985 | < 0.900 | cm³/m²/24 hr |
| 用量 | 12.0 µm | Internal Method | 59.5 | m²/kg |
| 23.0 µm | Internal Method | 31.0 | m²/kg |
| 水蒸气透过性 | 37.8°C, 90%RH, 23 µm | ASTM F1249 | < 0.70 | g/m²/24 hr |
| 37.8°C, 90%RH, 12 µm | ASTM F1249 | < 0.80 | g/m²/24 hr |
| Optical Density | 12.0 µm | Internal Method | | % |
| 23.0 µm | Internal Method | -2.8 到 7.2 | % |