| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能
|
收缩率
| 流动: 150°C, 30分钟, 0.0100 mm | ASTM D1204 | 2.5 | % |
| 流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 2.5 | % |
| 横向流动: 150°C, 30分钟, 0.0100 mm | ASTM D1204 | 0.4 | % |
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.4 | % |
| | 表面张力 | Metallized side (10.0 µm) | ASTM D2578 | 56 | dyne/cm |
| | Metallized side (12.0 µm) | ASTM D2578 | 56 | dyne/cm |
薄膜
| 薄膜厚度 - 经测试 | | | 10,12 | µm |
| 可供应的薄膜厚度 | | | 10,12 | µm |
抗张强度
| MD: 断裂, 10 µm | ASTM D882 | 206 | MPa |
| MD: 断裂, 12 µm | ASTM D882 | 206 | MPa |
| TD: 断裂, 10µm | ASTM D882 | 216 | MPa |
| TD: 断裂, 12 µm | ASTM D882 | 216 | MPa |
| 伸长率 | MD: 断裂, 10 µm | ASTM D882 | 100 | % |
| MD: 断裂, 12 µm | ASTM D882 | 100 | % |
| TD: 断裂, 10 µm | ASTM D882 | 90 | % |
| TD: 断裂, 12 µm | ASTM D882 | 90 | % |
| 透氧率 | (23°C, 10 µm) | ASTM D3985 | 0.700 | cm³/m²/24 hr |
| (23°C, 12 µm) | ASTM D3985 | 0.800 | cm³/m²/24 hr |
| 用量 | 10.0 µm | Internal Method | 71.4 | m²/kg |
| 12.0 µm | Internal Method | 59.5 | m²/kg |
| 水蒸气透过性 | 37.8°C, 90%RH, 10 µm | ASTM F1249 | 0.40 | g/m²/24 hr |
| 37.8°C, 90%RH, 12 µm | ASTM F1249 | 0.50 | g/m²/24 hr |
| Optical Density | 10.0 µm | Internal Method | | % |
| 12.0 µm | Internal Method | -2.4 到 7.6 | % |