性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 密度 | | ASTM D-1505 | 0.94 | g/cm3 |
熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 3.6 | g/10min |
机械性能 | 环境应力开裂 | 10% Igepal,Rotational Molded,F50 | ASTM D-1693A | 480 | hr |
环境应力开裂 | 100% Igepal,Rotational Molded,F50 | ASTM D-1693A | 1000 | hr |
拉伸屈服强度 | 3.18mm,Rotational Molded | ASTM D-638 | 17.9 | MPa |
弯曲模量-1% Secant | 3.18mm,Rotational Molded | ASTM D-790 | 758 | MPa |
热性能 | 热变形温度 | 0.45MPa,Unannealed,3.18mm,Rotational Molded | ASTM D-648 | 52 | ℃ |
热变形温度 | 1.8MPa,Unannealed,3.18mm,Rotational Molded | ASTM D-648 | 40 | ℃ |