| 性能项目 | 测试方法 | 试验条件[状态] | 测试数据 | 数据单位 |
| 性能 | 拉伸强度 | ASTM D638 | | 22.0
152 | kpsi Mpa |
| 拉伸模量 | ASTM D638 | | 650
4.5 | kpsi GPa |
| 拉伸伸长率 | ASTM D638 | | 7.6 | % |
| 挠曲强度 | ASTM D790 | | 34.9
244 | kpsi Mpa |
| 挠曲模量 | ASTM D790 | | 730
5.0 | kpsi GPa |
| 压缩强度 | ASTM D695 | | 32.1
221 | kpsi Mpa |
| 剪切强度 | ASTM D732 | | 18.5
128 | kpsi Mpa |
| | 悬臂梁式冲击，有缺口 | ASTM D256 | | 2.7
140 | ft-lb/in J/m |
| | 悬臂梁式冲击，无缺口 | ASTM D4812 | | 20
1060 | ft-lb/in J/m |
| | 热变形温度 | 264psi,ASTM D 648 | | 278
532 | ℃ ℉ |
| | CLTE3 | ASTM D 696 | | 31
17 | ppm/℃ ppm/℉ |
| | 体积电阻率 | ASTM D 257 | | 2X107 | ohm-cm |
| | 比重 | ASTM D 792 | | 1.42 | |
| | 吸水性，24小时 | ASTM D 570 | | 0.33 | % |
| | 摩擦系数，干摩擦50fpm（0.25m/s) | ASTM D 3702 | | 0.31 | |
| | 摩擦系数，干摩擦800fpm(4m/s) | ASTM D 3702 | | 0.29 | |
| | 摩损系数，干摩擦350fpm（0.25m/s) | ASTM D 3702 | | 13
23 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| | 摩损系数，干摩擦3800fpm(4m/s) | ASTM D 3702 | | 18
32 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| | 摩损系数，润滑环境4 | ASTM D 3702 | | 7
12 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |