| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D792 | 0.928 | g/cm3 |
| 熔流率 | 200℃/5.0kg | ASTM D1238 | 12 | g/10 min |
| 溶液粘度 | | ASTM D2196 | 880 | mPa·s |
| Styrene Content | | Internal Method | 18.0 | wt% |
| 灰含量 | | ASTM D1416 | 0.3 | wt% |
| 机械性能 | 硬度计硬度 | 邵氏 A, 1 秒 | ASTM D2240 | 39 | |
| 拉伸应力 | 300%应变, 25℃ | ASTM D412 | 1.65 | MPa |
| 抗张强度 | 屈服, 25℃ | ASTM D412 | 32.4 | MPa |
| 伸长率 | 断裂, 25℃ | ASTM D412 | 1400 | % |
| 应力松弛 | Peak Force @ 200% strain (A): 23℃, 889.0 µm | | 1.10 | MPa |
| Peak Force @ 500% strain: 23℃, 889.0 µm | 2.28 | MPa |
| Ratio (A:B): 23℃, 889.0 µm | 2.60 | |
| Relaxation @ 200% strain: 23℃, 889.0 µm | 6.0 | % |
| Set after 500% strain: 23℃, 889.0 µm | 16 | % |
| Unload @ 50% strain (B): 23℃ 889.0 µm | 0.414 | MPa |
| 补充信息 | Diblock Content | | Internal Method | < 1.0 | wt% |
| 挥发性 | | Internal Method | 0.2 | wt% |