| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 密度 | | ASTM D792 | 1.20 | g/cm³ |
| | | | ASTM D792 | 1.19 | g/cm³ |
| | 特定体积 | | ASTM D792 | 0.830 | cm³/g |
| | 熔流率 | (300°C/1.2 kg) | ASTM D1238 | 17.5 | g/10 min |
| | 收缩率 - 流动 | (3.20 mm) | Internal Method | 0.50到 0.70 | % |
| | 吸水率 | 24 hr | ASTM D570 | 0.15 | % |
| | | ASTM D570 | 0.35 | % |
| | 平衡, 100°C | ASTM D570 | | % |
| | 室外适用性 | | UL 746C | f2 | |
| 硬度 | 洛氏硬度 | M 计秤 | ASTM D785 | 70 | |
| | | R 计秤 | ASTM D785 | 110 | |
| 机械性能 | 抗张强度 | 屈服,Type I, 5 mm/min | ASTM D638 | 62.1 | MPa |
| | | 断裂,Type I, 5 mm/min | ASTM D638 | 65.5 | MPa |
| | 伸长率 | 屈服,Type I, 5 mm/min | ASTM D638 | 7.0 | % |
| | | 断裂,Type I, 5 mm/min | ASTM D638 | 110 | % |
| | 弯曲模量 | 50.0 mm 跨距,1.3 mm/min | ASTM D790 | 2340 | MPa |
| | 弯曲强度 | 屈服, 50.0 mm 跨距,1.3 mm/min | ASTM D790 | 93.1 | MPa |
| | 抗泰伯磨耗 | (1000 Cycles, 1000 g, CS-17 转轮) | ASTM D1044 | 10.0 | mg |
| 冲击性能 | 简支梁缺口冲击强度 | | ISO 179/1eA | 12 | |
| | | 23°C,80*10*3 sp=62mm | ISO 179/1eA | 65 | kJ/m² |
| | 简支梁缺口冲击强度 | -30°C,80*10*3 sp=62mm | ISO 179/1eU | 无断裂 | |
| | | 23°C,80*10*3 sp=62mm | ISO 179/1eU | 无断裂 | |
| | 悬壁梁缺口冲击强度 | 23°C | ASTM D256 | 600 | J/m |
| | | -30°C,80*10*3 | ISO 180/1A | 11 | kJ/m² |
| | | 23°C,80*10*3 | ISO 180/1A | 65 | kJ/m² |
| | 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m |
| | | -30°C,80*10*3 | ISO 180/1U | 无断裂 | |
| | | 23°C,80*10*3 | ISO 180/1U | 无断裂 | |
| | 落锤冲击 | (23°C) | ASTM D3029 | 169 | J |
| | 拉伸冲击强度 | Type S | ASTM D1822 | 546 | kJ/m² |
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 138 | °C |
| | | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 | °C |
| | 维卡软化温度 | 标准 B (120°C/h), 压 力2 (50N) | ASTM D1525 | 154 | °C |
| | Ball Pressure Test | (125°C) | | Pass | IEC 60695-10-2 |
| | 线形膨胀系数 | 流动: -40 到 95°C | ASTM E831 | 0.000068 | cm/cm/°C |
| | 比热 | | ASTM C351 | | |
| | 导热系数 | | ASTM C177 | 0.25 | W/m/K |
| | RTI Elec | | UL 746 | 80.0 | °C |
| | RTI Imp | | UL 746 | 80.0 | °C |
| | RTI Str | | UL 746 | 80.0 | °C |
| 电气性能 | 体积电阻率 | | ASTM D257 | > 1.0E+17 | ohm·cm |
| | 介电强度 | (3.20 mm, in Air) | ASTM D149 | 15 | kV/mm |
| | 介电常数 | 50 Hz | ASTM D150 | 3.17 | |
| | | 60 Hz | ASTM D150 | 3.17 | |
| | | 1 MHz | ASTM D150 | 2.96 | |
| | 耗散因数 | 50 Hz | ASTM D150 | 0.00090 | |
| | | 60 Hz | ASTM D150 | 0.00090 | |
| | | 1 MHz | ASTM D150 | 0.010 | |
| | 相比耐漏电起痕指数(CTI) | | UL 746A | 3 | PLC code |
| | 高电弧燃烧指数(HAI) | | UL 746A | 1 | PLC code |
| | 热丝引燃 (HWI) | | UL 746A | 3 | PLC code |
| 可燃性 | UL 阻燃等级 (1.20mm) | | | | UL 94 |
| | 灼热丝易燃指数 | 0.750 mm | IEC 60695-2-12 | 750 | °C |
| | | 1.50mm | IEC 60695-2-12 | 850 | °C |
| | 热灯丝点火温度 | 0.750 mm by VDE | IEC 60695-2-13 | 875 | °C |
| | | 1.50 mm | IEC 60695-2-13 | 850 | °C |
| 注射 | 干燥温度 | | | 120 | °C |
| | 干燥时间 | | | 3到4 | hr |
| | 干燥时间，最大 | | | 48 | hr |
| | 建议的最大水分含量 | | | 0.02 | % |
| | 建议注入量 | | | 40到60 | % |
| | 螺筒后部温度 | | | 260 到 280 | °C |
| | 螺筒中部温度 | | | 270 到 295 | °C |
| | 螺筒前部温度 | | | 280 到 305 | °C |
| | 射嘴温度 | | | 275 到 300 | °C |
| | 加工（熔体）温度 | | | 280 到 305 | °C |
| | 模具温度 | | | 70到95 | °C |
| | 背压 | | | 0.3到0.7 | MPa |
| | 螺杆转速 | | | 40 到 70 | rpm |
| | 排气孔深度 | | | 0.025 到 0.076 | mm |