| 性能项目 | 测试方法 | 试验条件[状态] | 测试数据 | 数据单位 |
| 性能 | 拉伸强度 | ASTM D638 | | 16.4
113 | kpsi Mpa |
| 拉伸模量 | ASTM D638 | | 990
6.8 | kpsi GPa |
| 拉伸伸长率 | ASTM D638 | | 3.3 | % |
| 挠曲强度 | ASTM D790 | | 31.2
215 | kpsi Mpa |
| 挠曲模量 | ASTM D790 | | 1000
6.9 | kpsi GPa |
| 压缩强度 | ASTM D695 | | 24.1
166 | kpsi Mpa |
| 剪切强度 | ASTM D732 | | 16.1
111 | kpsi Mpa |
| | 悬臂梁式冲击，有缺口 | ASTM D256 | | 1.2
64 | ft-lb/in J/m |
| | 悬臂梁式冲击，无缺口 | ASTM D4812 | | 8
410 | ft-lb/in J/m |
| | 热变形温度 | 264psi,ASTM D 648 | | 279
534 | ℃ ℉ |
| | CLTE3 | ASTM D 696 | | 25
14 | ppm/℃ ppm/℉ |
| | 体积电阻率 | ASTM D 257 | | 8X1015 | ohm-cm |
| | 比重 | ASTM D 792 | | 1.46 | |
| | 吸水性，24小时 | ASTM D 570 | | 0.28 | % |
| | 摩擦系数，干摩擦50fpm（0.25m/s) | ASTM D 3702 | | 0.31 | |
| | 摩擦系数，干摩擦800fpm(4m/s) | ASTM D 3702 | | 0.39 | |
| | 摩损系数，干摩擦350fpm（0.25m/s) | ASTM D 3702 | | 14
24 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| | 摩损系数，干摩擦3800fpm(4m/s) | ASTM D 3702 | | 17
30 | 10-10in3min/ft-lb-hr 10-8mm3/Nm |
| | 摩损系数，润滑环境4 | ASTM D 3702 | | | 10-10in3min/ft-lb-hr 10-8mm3/Nm |